Reliance Industries Limited
|
|
POLYPROPYLENE
|
| REPOL B120MA |
IMPACT COPOLYMER |
| |
| Product description &
applications : |
Features : |
|
REPOL Polypropylene B120MA is manufactured
using Unipol PP process which combines the production
efficiency of gas phase fluidized bed reactor technology
with the high activity and stereo specificity of the
SHAC catalyst system.
REPOL B120MA is recommended for use in
Injection Moulding processes where medium impact strength
is required. It is an ideal material for housewares,
thermowares, sanitarywares, furniture, industrial and
automotive components. making blow moulded containers,
sheets, automotive trims etc.
|
Repol B120MA
is designed to provide :
- High flow behaviour
- Good stiffness-impact balance
- Good surface gloss
- Low static charge build up and reduced dust pickup.
|
| |
| Typical properties
of Repol B120MA are as follows: |
| |
| Property |
ASTM Test
Method |
Unit |
Typical Value*. |
| Melt flow index,(230oc/2.16Kg) |
D 1238 |
g/10 min |
12.0 |
| Tensile Strength
at yield (50 mm/min ) |
D 638$ |
MPa |
24 |
| Elongation at
yield (50 mm/min ) |
D 638$ |
% |
10 |
| Flexural modulus
(1% secant) |
D 790A$ |
MPa |
1000 |
| Notched izod
impact strength (23oc) |
D 256$ |
J/m |
70 |
| Heat deflection
temperature (455 kPa) |
D 648 |
oC |
95 |
| |
|
$ : ASTM D638 Type I specimen injection
moulded and tested in accordance with ASTM D4101.
|
|
|
|
Repol B120MA meets the requirements
stipulated in IS 10910-1984 on on "Specification for
Polypropylene and its copolymers for safe use in contact
with foodstuffs, pharmaceuticals, and drinking water".
Additives incorporated in this grade conform to the
positive list of constituents as prescribed in IS-10909-1984.The
grade and the additives incorporated in it also comply
with the FDA:CFR Title 21, 177.1520, Olefin polymers.
|
|
|
|
REPOL is the registered trademark for
Polypropylene from Reliance Industries Limited
|
|
|
|
* Typical values with injection moulded
specimens, not to be taken as specification
|
|
The data, information and suggestions
contained contained herein are given purely as a guide.
Reliance Industries Limited and Reliance Group Companies
undertake no responsibility either for the results deriving
from their adoption or for possible position in apparent
contrast with existing patent rights.
|