Properties
|
Test Method
|
Unit
|
SJ-560S
|
|
Melt Flow
Rate (MFR) 230 °C
|
ASTM D-1238
|
g/10min
|
18.0
|
|
Mold Shrinkage
|
HPC Method
|
%
|
1.7
|
|
Density
|
ASTM D-1505
|
g/cm3
|
0.9
|
|
Tensile Strength
at Yield
|
ASTM D-638
|
Kg/cm2
|
300
|
|
Ultimate Elongation
|
ASTM D-638
|
%
|
>200
|
|
Flexural Modulus
of Elasticity
|
ASTM D-790
|
Kg/cm2
|
13,000
|
|
Hardness (Rockwell)
|
ASTM D-785
|
R
|
95
|
|
IZOD Impact
Strength (23 °C)
|
ASTM D-256
|
Kg-cm/cm
|
5.5
|
|
IZOD Impact
Strength (-10 °C)
|
ASTM D-256
|
Kg-cm/cm
|
2.0
|
|
Du-Pont Impact
Strength(23 °C)
|
HPC Method
|
Kg-cm
|
50
|
|
Heat Distortion
Temperature (4.6Kgf)
|
ASTM D-648
|
°C
|
95
|
|
HAZE (2mm)
|
ASTM D-746
|
%
|
15
|