Properties
|
Test Method
|
Unit
|
B-310
|
|
Melt Flow
Rate (MFR) 230 °C
|
ASTM D-1238
|
g/10min
|
0.5
|
|
Density
|
ASTM D-1505
|
g/cm3
|
0.9
|
|
Tensile Strength
at Yield
|
ASTM D-638
|
Kg/cm2
|
270
|
|
Ultimate Elongation
|
ASTM D-638
|
%
|
>500
|
|
Flexural Modulus
of Elasticity
|
ASTM D-790
|
Kg/cm2
|
13,000
|
|
Hardness (Rockwell)
|
ASTM D-785
|
R
|
93
|
|
IZOD Impact
Strength (-10°C)
|
ASTM D-256
|
Kg-cm/cm
|
35
|
|
IZOD Impact
Strength (23°C)
|
ASTM D-256
|
Kg-cm/cm
|
4.0
|
|
Du-Pont Impact
Strength (-10°C)
|
HPC Method
|
Kg-cm
|
80
|
|
Heat Distortion
Temperature
|
ASTM D-648
|
°C
|
109
|
|
Du-Pont Impact
Strength (23°C)
|
HPC Method
|
Kg-cm
|
200
|
|
Mold Shrinkage
|
HPC Method
|
%
|
1.80
|
Resin
Datasheets