L 81402 S is a High
Performance blown film LLDPE grade produced
by the latest generation Spherilence Gas
Phase Technology. The precise morphological
control achieved during polymerization confers
excellent balance of processability, performance
properties and improved properties not avaible
in conventional butene-1 based LLDPE.
L 81402 S is widely used in films for
general-purpose packaging, agricultural
and food contact application.
|
- Good Anti-blocking & Slip
properties
- For Monolayer & Multilayer Films
- Exceptional Processability
- High Mechanical Properties
- Food Contact Application
|
| |
| Properties |
Unit |
Test Method |
Value |
|
Melt Flow Index
(2.16 kg,190 C)
|
g/10
min |
ASTM
D 1238 |
2.0 |
| Density |
g/cm3 |
ASTM
D 1505 |
0.913 |
|
|
| FILM PROPERTIES (25 mm,
BUR =2.5) |
| Yield
Strength (MD/TD) |
MPa |
ASTM
D 882 |
10.5/9.5 |
| Tensile
Strength @ Break (MD/TD) |
MPa |
ASTM
D 882 |
29.5/25 |
| 2%
Secant Modulus (MD) |
MPa |
ASTM
D 882 |
162/188 |
| Elongation @
Break (MD/TD) |
% |
ASTM
D 882 |
715/765 |
| Dart
Impact Strength |
g |
ASTM
D 1709 |
90 |
| Elmendorf
Tear Strength (MD/TD) |
oC |
ASTM
D 1525 |
180/400 |
| |
| Recommended
Temperature profile oC
155/165/175/185-190/195/200 |
| Melt
Temperature |
oC |
|
190-210 |
| Blow
up Ratio |
|
|
2.0-3.0 |
| Die
Gap |
mm |
|
2.0-2.5 |
| |
|
The data presented above
are typical values and does not account
for testing variances. These should
not be constructed as specifications.
HPL does not guarantee the extract replication
of the data by users since plastics testing
is affected by a number of extraneous factors.
|