L
81401 S is a High
Performance blown film LLDPE
grade produced by the latest
generation Spherilence Gas
Phase Technology. The
precise morphological
control achieved during
polymerization confers
excellent balance of
processability, performance
properties and improved
properties not avaible in
conventional butene-1 based
LLDPE.
L 81401 S is widely used
in films for
packaging, liners, trash
bags and food contact
application.
|
- Good
Anti-blocking & Slip
properties
- For Monolayer &
Multilayer Films
- Exceptional
Processability
- High Mechanical
Properties
- Food Contact
Application
|
| |
| Properties |
Unit |
Test
Method |
Value |
|
Melt
Flow Index
(2.16 kg,190 C)
|
g/10
min |
ASTM
D 1238 |
0.95 |
| Density |
g/cm3 |
ASTM
D 1505 |
0.913 |
|
| FILM
PROPERTIES (25 mm,
BUR =2.5) |
| Yield
Strength (MD/TD) |
MPa |
ASTM
D 882 |
11.9/11.2 |
| Tensile
Strength @ Break (MD/TD) |
MPa |
ASTM
D 882 |
49/34.3 |
| 2%
Secant Modulus (MD) |
MPa |
ASTM
D 882 |
189/196 |
| Elongation @
Break (MD/TD) |
% |
ASTM
D 882 |
800/1000 |
| Dart
Impact Strength |
g |
ASTM
D 1709 |
120 |
| Elmendorf
Tear Strength (MD/TD) |
oC |
ASTM
D 1525 |
180/490 |
| |
| Recommended
Temperature profile
oC
175/185/195/205-210/215/220 |
| Melt
Temperature |
oC |
|
190-220 |
| Blow
up Ratio |
|
|
2.0-3.0 |
| Die
Gap |
mm |
|
2.0-2.5 |
| |
|
The data
presented above are typical
values and does not account
for testing variances.
These should not be
constructed as
specifications. HPL
does not guarantee the
extract replication of the
data by users since plastics
testing is affected by a
number of extraneous
factors.
|